The influence of the oxygen exposure on the thermal faceting of W[1 1 1] tip

The oxygen induced faceting of the macroscopic W[1 1 1] tip has been studied for oxygen exposures in the range 0.5–31 L and annealing temperatures 800–1800 K using the field ion microscopy (FIM) technique. After annealing at temperatures lower than 800 K, higher than 1850 K or for exposures lower than 0.5 L faceting was not observed. For exposures 0.5–1.9 L and annealing temperatures 800–1600 K well developed {1 1 2} facets with sharp edges formed. For exposures higher than 2.0 L edges of the {1 1 2} facets were broadening and disappearing, what has been attributed to the formation of three-dimensional tungsten oxides. The oxides could be easily removed by annealing the tip at 1700 K, what leads to formation of sharp facet edges. On the basis of these results a modified procedure of the ultrasharp tip fabrication has been proposed