High work function of Al-doped zinc-oxide thin films as transparent conductive anodes in organic light-emitting devices

Deposition of Al-doped ZnO (AZO) films with various film thicknesses on glass substrates was performed to investigate the feasibility of using AZO films as anode electrodes in organic light-emitting devices (OLEDs). The electrical resistivity of the AZO films with a 180-nm thickness was 4.085 10 2 V cm, and the average optical transmittance in the visible range was 80.2%. The surface work function for the AZO films, determined from the secondary electron emission coefficients obtained with a focused ion beam, was as high as 4.62 eV. These results indicate that AZO films grown on glass substrates hold promise for potential applications as anode electrodes in high-efficiency OLEDs