Effects of hydrogen flux on the properties of Al-doped ZnO films sputtered in Ar + H2 ambient at low temperature

Al-doped ZnO (AZO) transparent conductive thin films were grown by magnetron sputtering with AZO (98 wt.% ZnO, 2 wt.% Al2O3) ceramic target in Ar + H2 ambient at a relatively low temperature of 100 8C. To investigate the dependence of crystalline and properties of as-grown AZO films on the H2-flux, X-ray diffraction (XRD), X-ray photoemission spectrometer (XPS), Hall and transmittance spectra measurements were employed to analyze the AZO samples deposited with different H2-flux. The results indicate that H2-flux has a considerable influence on the transparent conductive properties of AZO films. The resistivity of 4.15 10 4 V cm and the average transmittance of more than 94% in the visible range were obtained with the optimal H2-flux of 1.0 sccm. Such a low temperature growing method present here may be especially useful for some low-melting point photoelectric devices and substrates.