The surface modified composite layer formation with boron carbide particles on magnesium alloy surfaces through pulse gas tungsten arc treatment

A novel fabrication process of surface modified composite layer by pulse current gas tungsten arc (GTA) surface modification process was used to deposit B4C particles on the surface of magnesium alloy AZ31. This method is an effective technique in producing a high performance surface modified composite layer. During the pulse current GTA surface modification process, considerable convection can exist in the molten pool due to various driving forces and the pulse current could cause violent stirring in the molten pool, and the large temperature gradient across the boundary between the GTA modified surface and matrix metal resulted in rapid resolidification with high cooling rates in the molten pool, so that the process result notable grain refinement in the GTA surface modified composite layer. The hardness and wear resistance of the GTA surface modified composite layer are superior to that of as-received magnesium alloy AZ31. The hardness values and wear resistance of GTA surface modified composite layer depend on the GTA process parameters and the B4C particles powder concentration and distribution. The optimum processing parameters for the formation of a homogeneous crack/defect-free and grain refinement microstructure were established