Ordered nano-scale domains in lithium niobate single crystals via phase-mask assisted all-optical poling

We report the formation of directionally ordered nano-scale surface domains on the +z face of undoped congruent lithium niobate single crystals by using UV illumination through a phase mask of sub-micron periodicity with an energy fluence between 90 mJ/cm2 and 150 mJ/cm2 at l = 266 nm. We clearly show here that the UV-induced surface ferroelectric domains only nucleate at and propagate along maxima of laser intensity. Although the domain line separation varies and is greater than 2 mm for this set of experimental conditions, this enables a degree of control over the all-optical poling process