Bio-functionalization of polycaprolactone infiltrated BCP scaffold with silicon and fibronectin enhances osteoblast activity in vitro

The surface property of a biomaterial plays a fundamental role in cell attachment, proliferation, differentiation, resorption, and biomolecular expression. In this study, the surface of a polycaprolactone-infiltrated biphasic calcium phosphate scaffold was biofunctionalized by silicon (Si) and fibronectin (FN) coating to evaluate the osteoblast-like cells activity in vitro. The surfaces of all scaffolds were characterized by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS), whereas the presence of the functional group was determined by Fourier-transform infrared spectroscopy (FT-IR). Coomassie brilliant blue staining was applied to confirm the presence of FN on the scaffold surface. The in vitro bioactivity of the osteoblast-like cells was determined by one cell morphology and proliferation assay at 3, 7, and 14 days by SEM. Cell viability assay by MTT showed higher cell viability rate on coated scaffolds than in those coated with Si only or non-coated surfaces. The mRNA expressions of alkaline phosphatase (ALP) and osteocalcin (OC) were determined using RT-PCR and the expressions of osteopontin (OPN), type I collagen, and osteocalcin (OC) proteins were determined using Western blot. Thus the expression of genes and proteins further confirmed both early and intermediate phases of osteoblast-like cell activity which was found increased by Si-and Fn coating on PCL infiltrated BCP surfaces.