Mechanical and electrical properties of GeSb2Te4 film with external voltage applied

A GeSb2Te4 (GST) film was deposited by RF magnetron sputtering with microwave electron cyclotron resonance plasma chemical vapor deposition equipment. Mechanical and electrical properties together with the morphologies of the film were studied by a nanoindenter which was equipped with nano-electrical contact resistance (nano-ECR) tool and atomic force microscope (AFM). Results show that when no voltage applied between sample and indent tip during indenting, the pile-up phenomenon was observed, the hardness and elastic modulus increases with the load mainly due to the underestimate of the contact area; when external voltages of −7 V, −8 V, −9 V, −10 V were applied, the resistance of the film decreased with applied voltages in about four orders of magnitude, while the elastic modulus increased from 159 GPa to 233 GPa, this changing in mechanical and electrical properties demonstrated that phase change happen during intending, a shrinking region with radius of about 2.5 μm was observed around the indentation when −8 V applied. Furthermore, indent load can also promote the phase change at given negative voltage.