Synthesis of molybdenum silicide by both ion implantation and ion beam assisted deposition

Two groups of Mo/Si films were deposited on surface of Si(1 0 0) crystal. The first group of the samples was prepared by both ion beam assisted deposition (IBAD) and metal vapor vacuum arc (MEVVA) ion implantation technologies under temperatures from 200 to 400 °C. The deposited species of IBAD were Mo and Si, and different sputtering Ar ion densities were selected. The mixed Mo/Si films were implanted by Mo ion with energy of 94 keV, and fluence of Mo ion was 5 × 1016 ions/cm2. The second group of the samples was prepared only by IBAD under the same test temperature range. The Mo/Si samples were analyzed by X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), sheet resistance, nanohardness, and modulus of the Mo/Si films were also measured. For the Mo/Si films implanted with Mo ion, XRD results indicate that phase of the Mo/Si films prepared at 400 and 300 °C was pure MoSi2. Sheet resistance of the Mo/Si films implanted with Mo ion was less than that of the Mo/Si films prepared without ion implantation. Nanohardness and modulus of the Mo/Si films were obviously affected by test parameters.