The characterization of mechanical and surface properties of poly (glycerol–sebacate–lactic acid) during degradation in phosphate buffered saline

The present study synthesized a poly (glycerol–sebacate–lactic acid) (PGSL) with 1:1:0.5 mole ratio of glycerol, sebacate and lactic acid and investigated the degradation characteristics of the polymer in phosphate buffered saline (PBS) at 37 °C in vitro by means of mass loss tests, geometry, differential scanning calorimeter (DSC) measurements, tensile analysis and scanning electron microscopy (SEM). The maintained geometry, linear mass loss, and minor crack formation on the surface during degradation characterized both the bulk degradation and surface erosion of the polymer. By day 30 of degradation, the mass lost reached 16%. The elastic modulus, tensile strength and elongation at breakage of PGSL were correlative to the period of degradation.