Dry sliding wear behaviour of magnesium oxide and zirconium oxide plasma electrolytic oxidation coated magnesium alloy

Two types of PEO coatings, one consisting of magnesium oxide (MgO) and the other comprising zirconium oxide (ZrO2) as the main phase composition were produced on AM50 magnesium alloy from alkaline and acidic electrolytes, respectively. The ZrO2 coating was found to be spongy and thicker with a higher roughness, whilst the relatively more compact MgO coating was having contrasting features. In the dry sliding oscillating wear tests under two different loads viz., 2 N and 5 N, the ZrO2 coating exhibited a very poor wear resistance. The MgO coating showed an excellent resistance to sliding wear under 2 N load; however, the load bearing capacity of the coating was found to be insufficient to resist the wear damage under 5 N load. The higher specific wear rates of the MgO coating under 5 N load and that of the ZrO2 coating under 2 N and 5 N loads were attributed to the poor load bearing capacity and a three-body-abrasive wear mechanism.