Effect of swift heavy ion irradiation in Fe/W multilayer structures

Present study reports effect of swift heavy ion irradiation on structural and magnetic properties of sputtered Fe/W multilayer structures (MLS) having bilayer compositions of [Fe(20 Å)/W(10 Å)]5BL and [Fe(20 Å)/W(30 Å)]5BL. These MLS are irradiated by 120 MeV Au9+ ions up to fluence of 4 × 1013 ions/cm2. X-ray reflectivity (XRR), wide-angle X-ray diffraction (WAXD), cross-sectional transmission electron microscopy (X-TEM) and magneto optical Kerr effect (MOKE) techniques are used for structural and magnetic characterization of pristine and irradiated MLS. Analysis of XRR data using Parrattʹs formalism shows a significant increase in W/Fe interface roughness. WAXD and X-TEM studies reveals that intra-layer microstructure of Fe-layers in MLS becomes nano-crystalline on irradiation. MOKE study shows increase in coercivity at higher fluence, which may be due to increase in surface and interface roughness after recrystallization of Fe-layers.