Scattering effects of primary electrons in Co/Cu(1 1 1) measured by Auger; elastic and loss electrons

Electron energy losses were measured as a function of the incidence angle of the primary electron beam for the Co/Cu(1 1 1) adsorption system. The measurements performed for the clean and covered substrate reveal characteristic intensity maxima associated with the close packed rows of atoms, as it was observed in the so called directional Auger and directional elastic peak electron spectroscopy profiles. The incidence angle dependent signal of electron energy losses measured for the clean (Cu 3p3/2) and covered (Co 3p3/2) substrate gives the so called directional electron energy loss spectroscopy (DEELS) profiles which contain structural as well as chemical information. The scattering of primaries and different emission processes associated with electron energy losses, Auger, and elastically backscattered electrons are discussed. A change in the hCu (Cu M2,3VV transition) Auger signal recorded during the continuous cobalt deposition shows that the growth mode is not a pure layer by layer type. The complete covering of the substrate by Co at higher coverages is confirmed by the comparison between experimental and theoretical ratios of the Auger peak heights.