Preparation of silver nanoparticle containing silica micro beads and investigation of their antibacterial activity

Silver nanoparticle containing silica micro beads (Ag-NPBs) were successfully prepared by using sodium silicate, a cheap precursor, involving chemical reductive method. First, silica gel was synthesized and crushed into micro beads which have sizes ranging from 0.5 to 1 mm. Silica micro beads were then modified with 3-aminopropyltriethoxysilane to graft amino functional groups onto their surface. Silver ions were loaded onto the surface of the modified silica and reduced to silver crystal by adding NaBH4. The presence of silver nanoparticles as well as structure of materials was characterized with FT-IR, XRD, BET, FE-SEM, TEM, UV–vis spectrophotometer, and optical microscope. Silver nanoparticles with an average size about 5 nm were found in the pore and on the surface of amino functionalized silica beads. Ag-NPBs samples were tested for their antibacterial activity against Escherichia coli (E. coli). The antibacterial activity was examined by both zone inhibition and test tube test method. Biological results indicated that the synthesized materials have an excellent antibacterial performance against E. coli which was completely inhibited after 5 min contact with Ag-NPBs.