Degradation factors of a new long life cathode

This paper analyses the degradation factors of a new long life coated impregnated cathode after accelerated life test. The surface state of the cathode is investigated with scanning electron microscope (SEM) as well as the content and variation of the various elements on the surface and the longitudinal section of the cathode are analyzed with Auger electron spectroscopy (AES) before and after the life test. The analyzing results with SEM show that the cathode coating shrinks at the life end and leads to a rise in its work function. The analyzing results with AES show that the percent of the W increases and the active materials Ba decreases on the cathode surface at the life end. Furthermore, there is less Ba underneath the cathode surface but still a lot of Ba in the tungsten matrix at the life end.