Damage evolution behavior of CFRP laminates under post-impact fatigue with water absorption environment

In this study, the damage evolution behavior was evaluated considering the effect of the textile structure and water absorption. Damage observation was conducted by the integration of non-destructive and direct observation methods. Candidate textile reinforcements were T300-3k plain woven fabric (PW) and T700S-12k multi-axial knitted fabric (MA). The effect of water absorption on the performances of compression after impact (CAI) and PIF were small in PW CFRP laminates. Conversely, PIF properties of water-absorbed MA CFRP laminates drastically decreased than that of dry ones. CAI strength was not affected by water absorption. PIF performance of dry MA CFRP was fairly higher than that of the others. From the precise observation, some evidences of interfacial deterioration caused by water absorption were confirmed in both PW and MA CFRP laminates.