Intergranular corrosion behavior of the 7075-T6 aluminum alloy under different annealing conditions

The effect of annealing conditions producing various grain sizes on the intergranular corrosion behavior of high-strength aluminum alloy type 7075-T6 was investigated using electrochemical polarization techniques. Aluminum alloy specimens with large grain size exhibited lower breakdown potentials in deaerated 0.5 M NaCl solution. The breakdown potentials decreased with increasing grain size. Microscopic observations of the exposed surfaces during potentiostatic polarization testing showed that the coarse grain structure promotes intergranular crack growth.