Hydrothermally-induced morphological transformation of GdVO4:Eu3+

The aim of the present study is to investigate the effect of a wide pH range on morphology and luminescence properties of europium-doped gadolinium vanadate (GdVO4:Eu3+). GdVO4:Eu3+ powders were hydrothermally synthesized at 180 °C for 24 h in a wide pH range. The as-synthesized powders were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and photoluminescence (PL) spectroscopy. The XRD results showed that GdVO4:Eu3+ with the tetragonal structure formed at pH < 13 as a single phase and Gd(OH)3 formed at pH ≥ 13 as a secondary phase. The SEM and TEM observations demonstrated the hydrothermally-induced morphological transformation of GdVO4:Eu3+ powders by altering the pH of the synthesis solution. The possible mechanism for the morphological transformation was proposed. The intensities of the prominent peaks at 618 nm in the PL emission spectra of GdVO4:Eu3+ powders considerably shift according to the specific morphology. The luminescence intensity of the octahedron- and rod-like GdVO4:Eu3+ powders hydrothermally obtained at pH = 3 was the strongest one due to high packing density and high crystallinity as well as the extended reduction of the concentration of inherent defect states or adsorbed species.