In vitro solubility and bioactivity of Sr and Mg co-doped calcium phosphate glass-ceramics derived from different heat-treatment temperatures

CaO–P2O5–Na2O–SrO–MgO glass–ceramic system was prepared by controlled heat treatment process. Solubility and bioactivity of glass-ceramics were measured and evaluated in simulated body fluid (SBF) and cell culture medium respectively. The dissolution behavior of these glass-ceramics strongly depends on the amount and microstructure of the crystals precipitated by sintering treatment. Concerning the bioactivity, the onset of the apatite formation on the glass–ceramic system was directly dependent on the amount of bioactive glass amount which can be controlled using different temperatures of heat treatment. After immersing glass–ceramic in SBF, Mg ion as one of system composition can be released from residual glass and provides a high impact on the Ca/P ratio and chemical stability of the deposited apatite layer that directly affects cell attachment and proliferation in in vitro cell culture system. The glass ceramics heat-treated at 760 °C and 780 °C show less glass amount, and their degradation rates are both compatible with cell growth and differentiation.