EVA reactive blending with Si–H terminated polysiloxane by carbonyl hydrosilylation reaction: From compatibilised blends to crosslinking networks

A new and original method based on carbonyl hydrosilylation was developed to prepare ethylene-vinyl acetate (EVA)/polysiloxane polymer blends. This focused on the addition of hydrogenosilane groups (SiH) from polysiloxane to the carbonyl groups of EVA. The influence of the nature of the polysiloxane on blend properties was investigated by rheology and scanning electron microscopy. Mixing of a low viscosity polysiloxane with a high viscosity EVA matrix produced a two-phase morphology. The occurrence of the hydrosilylation reaction at the EVA/polysiloxane interface promoted a homogenisation of the blend depending on the molar ratio SiH/vinyl acetate groups, [SiH]/[VA], and the viscosity ratio of the blend. Two distinct behaviours were observed. The formation of a crosslinked network under shear was obtained for a low viscosity ratio between polysiloxane and EVA (λpolysiloxane/EVA = 4.0 × 10−6) with a high concentration of SiH groups ([SiH]/[VA] = 0.5), while the formation of a compatibilised blend was observed for high molar mass polysiloxanes (Mn > 15,000 g mol−1) with a low concentration of SiH ([SiH]/[VA] < 4.0 × 10−3).