Effect of high heating and cooling rate on interface of diffusion bonded gray cast iron to medium carbon steel

In the present study, a gray cast iron and a medium carbon steel couple were diffusion bonded at the temperatures of 850, 900, 950 and 1000 °C under a pressure of 8 MPa for 30 min, and the effects of temperature and high heating and cooling rate on interface formations and microstructure were investigated. After diffusion bonding, scanning electron microscopy, shear test measurements and microhardness measurement of interface region were made. The microstructure at the inside of medium carbon steel of bonded couple consisted of martensite. As a result, from the microstructural observations, a good bonding along the interface of the bonded couples and the interface is free from voids and microcracks.