Influence of equal channel angular extrusion processing parameters on the microstructure and mechanical properties of Mg–Al–Y–Zn alloy

An as-cast Mg–Al–Y–Zn alloy was successfully processed by equal channel angular extrusion (ECAE) in the temperature range of 225–400 °C, and the influences of processing temperature on the microstructure and mechanical properties were investigated. The use of back pressure during one-pass ECAE of Mg–Al–Y–Zn alloy was favorable for eliminating the undeformed area in the billet. At the processing temperature below 250 °C, the microstructures were characterized by unrecrystallised structure and the precipitated phase Mg17Al12 was elongated along the extrusion direction. With increasing processing temperature to 350 °C, a large number of recrystallised grains were obtained. Increasing processing temperature promoted workability but led to decrease in the strength of Mg–Al–Y–Zn alloy. Then billets of as-cast Mg–Al–Y–Zn alloy were extruded at different numbers of ECAE passes. It was found that the microstructure was effectively refined by ECAE and mechanical properties were improved with numbers of ECAE passes increasing from one-pass to four passes. However, strengths decreased slightly after five passes though the grain size decreased considerably.