Vibration cavitation behaviour of selected Ni–Mn–Ga alloys

Vibration cavitation erosion tests were carried out on Ni–Mn–Ga alloys of three different crystal structures: (1) the cubic austenite, (2) the non-modulated tetragonal martensite (T) and (3) the five-layered martensite (5M). All Ni–Mn–Ga alloys exhibited cavitation behaviour characterized by a step-wise curve of mass loss versus test time. This behaviour is correlated to the microstructural nature of the alloys as well as the surface conditions of the pre-test samples. The type and concentration of the defects at the surfaces were critical to the cavitation resistance of the alloys. The best cavitation resistant alloy was of a cubic austenitic structure, followed with the alloy of a tetragonal T-martensite. The largest material loss was found in the alloy with a 5M martensite. All the studied Ni–Mn–Ga alloys had an excellent cavitation resistance compared to that of the reference stainless steel, and they even excelled some NiTi alloys found in literature. This may be due to the superelasticity of the cubic austenite and the twinning of the martensitic phases.