Analysis of load-speed sensitivity of friction composites based on various synthetic graphites

The frictional response of a multi-component phenolic-based friction material is highly complex under a set of variable loads and speeds. The present paper discusses the sensitivity of friction coefficient (μ) of friction composites containing synthetic graphite with different particle sizes (with similar crystallinity range) to braking pressure and sliding speed. The friction studies were carried out on a sub scale brake-test-rig, following 4 loads × 3 speeds experimental design. The best combination of performance properties was observed for the composite containing synthetic graphite with an average particle size of 410 μm. Other particle sizes which resulted in good performance were 38 and 169 μm. Very fine particle sizes were not beneficial for desired combination of performance properties. Regression analysis of μ following an orthogonal L9(3 × 3) experimental design method revealed that the first order influences of sliding speed and braking pressure were significant. When all the combinatorial influences of braking pressure and sliding speed are taken into account together their simultaneous effects would be most effective in the range of graphite particle size ∼80–250 μm.