Influence of the carbon surface on cathode deposits in non-aqueous Li–O2 batteries Original Research Article

Cup-stacked carbon nanotubes (CSCNT) with different surface properties were used for the non-aqueous Li–O2 battery cathodes, and then examined at high magnification to understand how the discharge products were deposited on the cathode. As-prepared CSCNT based cathode had many reactive edges consisting of truncated conical graphene layers. After discharge, discharge products with average particle size 50 nm covered a nanotube, resulting in a layer-like texture. On the other hand, a heat-treated CSCNT based cathode was composed of edges terminated by graphitization of several graphene layers. After discharge, the size of the products was almost the same but the products were agglomerated, forming a bulky morphology. It was, thus, found that the carbon surface structure was closely related with the morphology of the cathode deposits after discharge. First principles calculations also indicated that no terminated edges acted as preferential active sites in adsorbing and storing the reaction species. It was, therefore, concluded that the active edges of the carbon surface were indispensable for controlling the morphology of cathode deposits and improving the battery performance.