Effects of proton irradiation on nanocluster precipitation in ferritic steel containing fcc alloying additions Original Research Article

Newly developed precipitate-strengthened ferritic steels with and without pre-existing nanoscale precipitates were irradiated with 4 MeV protons to a dose of ∼5 mdpa at 50 °C and subsequently examined by nanoindentation and atom probe tomography. Irradiation-enhanced precipitation and coarsening of pre-existing nanoscale precipitates were observed. Cu partitions to the precipitate core along with a segregation of Ni, Al and Mn to the precipitate/matrix interface after both thermal aging and proton irradiation. Proton irradiation induces the precipitation reaction and coarsening of pre-existing nanoscale precipitates, and these results are similar to a thermal aging process. The precipitation and coarsening of nanoscale precipitates are responsible for the changes in hardness. The observation of the radiation-induced softening is essentially due to the coarsening of the pre-existing Cu-rich nanoscale precipitates. The implication of the precipitation on the embrittlement of reactor-pressure-vessel steels after irradiation is discussed.