Changes in vibrational entropy during the early stages of chemical unmixing in fcc Cu–6% Fe

A nanocrystalline face-centered cubic (fcc) solid solution of 6% Fe in Cu was prepared by high-energy ball milling, and annealed at temperatures from 200 to 360 °C to induce chemical unmixing. The chemical state of the material was characterized by three-dimensional atom probe microscopy, Mössbauer spectrometry and X-ray powder diffractometry. The unmixing was heterogeneous, with iron atoms forming iron-rich zones that thicken with further annealing. The phonon partial density of states (pDOS) of 57Fe was measured by nuclear resonant inelastic X-ray scattering, showing the pDOS of the as-prepared material to be that of an fcc crystal. The features of this pDOS became broader in the early stages of unmixing, but only small changes in average phonon frequencies occurred until the body-centered cubic (bcc) phase began to form. The vibrational entropy calculated from the pDOS underwent little change during the early stage of annealing, but decreased rapidly when the bcc phase formed in the material.