Electrochemical and Structural Properties of xLi2MO3 ·(1-x)LiMn0.5Ni0.5O2 Electrodes for Lithium Batteries (M= Ti, Mn, Zr; 0xA0.3)

Electrochemical and structural properties of xLi2MʹO3 ·(1-x)LiMn0.5Ni0.5O2 electrodes (Mʹ= Ti, Mn, Zr; 0x 0.3) for lithium batteries are reported. Powder X-ray diffraction, lattice imaging by transmission electron microscopy, and nuclear magnetic resonance spectroscopy provide evidence that, for Mʹ = Ti and Mn, the Li2MʹO3 component is structurally integrated into the LiMn0.5Ni0.5O2 component to yield "composite" structures with domains having short-range order, rather than true solid solutions in which the cations are uniformly distributed within discrete layers. Li2TiO3 and Li2ZrO3 components are electrochemically inactive, whereas electrochemical activity can be induced into the Li2MnO3 component above 4.3 V vs Li0. When cycled in lithium cells, xLi2MnO3·(1-x) LiMn0.5Ni0.5O2 electrodes with x = 0.3 provide capacities in excess of 300 mA·h/g over the range 4.6 -1.45 V.