Semicrystalline morphology in thin films of poly(3-hexylthiophene)

The thermodynamic phase behavior and the morphology in thin films of poly(3hexylthiophene) (P3HT) has been studied using calorimetry, X-ray scattering, and scanning force microscopy (AFM). Around 225 °C a phase transition from the crystalline state to a layered, liquid crystalline structure occurs in regioregular P3HT, while the regiorandom counterpart material is disordered at all temperatures and displays a glass transition temperature Tg–3 °C. Regioregular P3HT is semicrystalline and forms needle or plate like crystallites which in solution cast thin films are oriented with respect to the substrate. Films produced by spin coating display a non-equilibrium structure with reduced order and orientation. Annealing of these films in the liquid crystalline state leads to the formation of a morphology similar to the one observed in solution cast films