Corrosion fatigue behavior of extruded magnesium alloy AZ31 in sodium chloride solution

In the present study, corrosion fatigue experiments were done using the extruded magnesium alloy AZ31 in the 3% sodium chloride solution to clarify the corrosion fatigue characteristics of the material. Corrosion fatigue lives greatly decreased as compared with those in laboratory air. It was also clarified that most of the corrosion fatigue life (70–80%) at the lower stress amplitude is occupied with the period of the corrosion pit growth. Corrosion fatigue lives were evaluated quantitatively by dividing the corrosion fatigue process into the following two periods, i.e. (1) the corrosion pit growth period preceding the crack initiation from the pit and (2) the crack growth period before the specimen failure. In the analysis, the law of the corrosion pit growth proposed by authors was used to deal with the above first period. The evaluated results corresponded well to the experimental results.