Acoustic emission study of fatigue crack closure of physical short and long cracks for aluminum alloy LY12CZ

Crack closure of physical short and long cracks of LY12CZ aluminum alloy during fatigue process was investigated using acoustic emission (AE) technique. Results showed that the effective fatigue crack growth curve (da/dN vs. ΔKeff) of physical short and long cracks obtained by the AE technique was consistent with the effective fatigue crack growth curve at high stress ratio (R = 0.8), which implied that the AE technique could measure the crack closure level, especially for physical short crack. The growth rate of physical short crack was much higher than that of long crack at the same ΔK, and the lower crack closure level of short crack was the main reason.