Abrasive wear behavior of Ni–P coated Si3N4 reinforced Al6061 composites

Ni–P coated Si3N4 reinforced Al6061 composites were fabricated by vortex method. Percentage of reinforcement was varied from 6 wt.% to 10 wt.% in steps of 2. Cast matrix alloy and developed composites were hot forged at a temperature of 500 °C using a 300T hydraulic hammer. Both as cast and hot forged matrix alloy and its composites were subjected to microstructure studies, grain size analysis, microhardness and abrasive wear tests. Microstructure studies reveal uniform distribution of silicon nitride particles with good bond between matrix and reinforcement in both as cast and hot forged condition. It is observed that, increased content of reinforcement in both as cast and hot forged composites do result in significant grain refinement. However, when compared with as cast matrix alloy and its composites hot forged alloy and its composites exhibits higher extent of grain refinement. Both as cast and hot forged composites exhibit improved microhardness and abrasive wear resistance when compared with the unreinforced alloys under identical test conditions. Abraded worn surfaces were examined using scanning electron microscopy (SEM) for possible wear mechanisms. Increased abrasive particle size and load has resulted in larger extent of grooving leading to increased abrasive wear loss for both the matrix alloy and developed composites.