Enhancement of abrasion and corrosion resistance of duplex stainless steel by laser shock peening

The results for laser shock peening of duplex stainless steel (22% Chromium–5% Nickel) using a pulsed Nd:YAG laser (wavelength = 532 nm, pulse width = 8 ns) for the application to high-capacity pumps for reverse-osmosis type seawater desalination plants are reported. By properly selecting the process parameters such as laser intensity of 10 GW/cm2, laser pulse density of 75 pulse/mm2, and 100 μm thick aluminum foil as a protective coating layer, wear volume and corrosion rate of duplex stainless steel could be reduced by 39% and 74.2%, respectively. The number and size of corrosion pits produced on wear track during copper accelerated acetic acid salt spray test decreased approximately by half as a result of laser shock peening. It is shown that laser shock peening is a practical option to improve abrasion and corrosion properties of a seawater desalination pump parts.