Thermal properties of poly(butylene oxalate) copolymerized with azelaic acid

Poly(butylene oxalate) (PBO) and poly(butylene oxalate/butylene azelate) random copolymers (PBOBAz) of various compositions were synthesized in bulk and characterized in terms of chemical structure and thermal properties. The thermal behavior was examined by thermogravimetric analysis and differential scanning calorimetry. All copolymers were found to be partially crystalline and thermally stable up to about 290 °C. The main effect of copolymerization was a decrease in melting and glass transition temperatures with respect to PBO homopolymer. The pure crystalline phase characteristic of PBO was evidenced by means of X-ray measurements in all the copolymers under investigation. The fusion temperatures appeared to be well correlated to composition by Baurʹs equation. Amorphous samples were obtained after melt quenching and showed a monotonic decrease of glass transition temperatures as the content of the flexible butylene azelate units is increased. Fox equation described well the Tg–composition data. Lastly, the overall crystallization rate of PBO was found to decrease regularly with increasing butylene azelate unit content.