Poly(ethylene-2,6-naphthalate) microfiber prepared by carbon dioxide laser-thinning method

Poly(ethylene-2,6-naphthalate) (PEN) microfiber was continuously obtained by using a carbon dioxide (CO2) laser-thinning method. As a winding speed increased, the fiber diameter decreased, and its birefringence increased. When the PEN microfiber, obtained by irradiating the laser operated at a power density of 9.15 W cm−2 to the original fiber supplied at 0.33 m min−1, was wound up at 1594 m min−1, the obtained microfiber had a diameter of 2.8 μm, a birefringence of 0.174, tensile modulus of 5.4 GPa, and a tensile strength of 0.36 GPa.