Effect of POSS on morphology and properties of poly(2,6-dimethyl-1,4-phenylene oxide)/polyamide 6 blends

Poly(2,6-dimethyl-1,4-phenylene oxide)/polyamide 6 (PPO/PA6) (50/50 w) blends filled with epoxycyclohexyl polyhedral oligomeric silsesquioxane (POSS) were prepared via melt-mixing. The reactions between POSS and PPO/PA6 blends were studied by Fourier transform infrared spectroscopy, end group and gel content tests. The morphology of PPO/PA6/POSS composites was observed by field emission scanning electron microscope and transmission electron microscope. As a chain extender and a crosslinking agent for PA6, POSS largely affected the morphology of the composites, which was mainly dependent on the melt-viscosity ratio and interfacial tension between the components. With increasing POSS content from 2 to 4 phr, the morphology of the composites transformed from droplet/matrix to co-continuous morphology. The PPO/PA6/POSS composites with co-continuous morphology had the better mechanical properties than those with droplet/matrix morphology. Dynamic mechanical thermal analysis showed that the addition of POSS increased the Tg of PA6.