Red electroluminescent process excited by hot holes in SrGa2S4:Ce, Mn thin film

This paper reports the first observation of red electroluminescence (EL) in SrGa2S4:Ce, Mn thin film. The EL spectrum consists of single broad emission band having a peak wavelength of 665 nm. The dominant EL decay time was 31 μs. The relationship between the applied voltage and the EL waveform was measured in single insulating thin film electroluminescent (TFEL) devices. An asymmetric EL waveform was observed in SrGa2S4:Ce, Mn TFEL devices under a rectangular applied voltage. The polarity of the EL waveform in these devices was different from the waveform in manganese-activated zinc sulfide ZnS:Mn devices. This indicates that hot holes excite the Mn2+ ions to cause the red EL.