Synthesis and characterization of ZnSe:Fe/ZnSe core/shell nanocrystals

High-quality ZnSe:Fe/ZnSe core/shell nanocrystals were prepared via a hydrothermal microemulsion technique. Effective surface passivation of monodisperse ZnSe:Fe nanocrystals is achieved by overcoating them with a ZnSe shell. The samples were characterized by means of XRD, EDX, TEM, PSD, XPS, photoluminescence, and Raman spectrum. The results show that the as-synthesized nanocrystals are cubic zinc blende ZnSe structure with high purity and the average particle size of ZnSe:Fe/ZnSe core/shell nanocrystal is larger than that of ZnSe:Fe core. The growth of ZnSe shell causes a small red shift in PL spectra, and then the PL quantum yield (QY) increases from 16% before shell growth to the maximum of 37% after increasing shell thickness up to 1.2 monolayers (ML). Moreover, both transverse optic (TO) and longitudinal optic (LO) phonon modes of ZnSe are shifted toward lower frequency as compared with the reported ones.