Secondary phases in Nb-doped BaTiO3 ceramics

In this work, the effect of Nb2O5 addition on the microstructure of BaTiO3 was studied. From XRD diagrams, a diminution in tetragonality parameters with an increase in dopant concentration was observed. In order to determine morphology and composition of secondary phases in niobium-doped barium titanate, EDAX and SEM analyses were carried out. It was found that a concentration of dopant higher than 0.15 mol% leads to fine-grained BaTiO3 without abnormal grain growth. Otherwise, compositions of secondary phases correspond to the titanium-rich region in the BaO–TiO2 phase diagram. Besides, the titanium content in the precipitate increases with the Nb2O5 addition.