Preparation of nanocrystalline ferroelectric CaBi4Ti4O15 by citrate gel method

A gel was formed when an aqueous solution of CaCl2, BiNO3, TiOCl2 and citric acid in stoichiometric ratio is heated on a water bath. This gel on decomposition at 700 °C produced nano crystallites of the ternary oxide, CaBi4Ti4O15 (CBT). The phase contents and lattice parameters were studied by the powder X-ray diffraction (XRD). Particle size and morphology was studied by transmission electron spectroscopy (TEM). The room temperature dielectric constant at 1 kHz is 390. The ferroelectric hysteresis loop parameters of these samples were also studied by a home-built Sawyer-tower circuit.