Nitrate–citrate combustion synthesis of Ce1−xGdxO2−x/2 powder and its characterization

The structure, thermal expansion coefficients, and electric conductivity of Ce1−xGdxO2−x/2 (x = 0–0.6) solid solution, prepared by the gel-combustion method, were investigated. The uniform small particle size of the gel-combustion prepared materials allows sintering into highly dense ceramic pellets at 1300 °C, a significantly lower temperature compared to that of 1600–1650 °C required for ceria solid electrolytes prepared by traditional solid state techniques. XRD showed that single-phase solid solutions formed in all the investigated range. The maximum conductivity, σ600 °C = 5.26 × 10−3 S/cm, was found at x = 0.2. The thermal expansion coefficient, determined from high-temperature X-ray data, was 8.125 × 10−6 K−1 at x = 0.2.