Effect of sintering temperature on compressive strength of porous yttria-stabilized zirconia ceramics

Porous yttria-stabilized zirconia (YSZ) ceramics were fabricated by tert-butyl alcohol (TBA)-based gel-casting method for potential applications in heat-insulation materials. The effect of sintering temperature on compressive strength of porous YSZ ceramics was investigated on the basis of measurements linear shrinkage, porosity and pore size. As the sintering temperature increased from 1350 to 1550 °C, a decrease of porosity from 77 to 65%, a decrease of average pore size from and an increase of linear shrinkage from 15.4 to 31.8% were observed. The compressive strength increased remarkably from 3 to 27 MPa with increasing sintering temperature from 1350 to 1550 °C, which was related to the corresponding change of linear shrinkage, porosity, pore size and microstructure. A remarkable decrease of compressive strength with increasing porosity was observed. The compressive strength decreased also with increasing pore size.