Optimizing the performance of porous electrochemical cells for flue gas purification using the DOE method

The DOE model was used to improve the performance of cells for electrochemical gas purification. Three factors were chosen: the amount of graphite, the Lanthanum Strontium Manganate/Gadolinium-doped Cerium oxide weight % ratio, and the Lanthanum Strontium Manganate pre-calcination temperature (with or without Lanthanum Strontium Manganate calcinated at 1000 °C). The effects of the following physical properties were measured: porosity, pore size, shrinkage, and conductivity. The sintered tapes were also characterized with scanning electron microscopy. Graphite was added as a pore former. The work shows, that a change in a factor not only changes the performance property that one would expect, but also influence other properties.