Sol–gel preparation and characterization of nano-crystalline lithium–mica glass–ceramic

The nano-crystalline lithium–mica glass–ceramic with separated crystallite size of 13 nm was prepared using sol–gel technique. In such a process, the structural evolutions and microstructural characteristics of the synthesized samples were investigated through X-ray diffraction, transmission electron microscopy, thermal analysis and Fourier transform infrared spectroscopy. It was found that the crystallite size of the mica obtained from sol–gel method is smaller than the one synthesized via conventional melted method. The XRD results also showed that the crystallization of mica occurred above 675 °C and it could originate from MgF2 so that the next stage will also be the transformation from mica to norbergite and norbergite to chondrodite. The activation energy of the crystallization and Avrami factor were measured as 376.7 kJ mol−1 and 2.3, respectively. It is found that the bulk crystallization could be considered as the predominant crystallization mechanism for the glass–ceramic.