Structure, dielectric and ferroelectric properties of 0.92Na0.5Bi0.5TiO3–0.06BaTiO3–0.02K0.5Na0.5NbO3 lead-free ceramics: Effect of Co2O3 additive

0.92Na0.5Bi0.5TiO3–0.06BaTiO3–0.02K0.5Na0.5NbO3+x wt% Co2O3 (NBKT–xCo, x=0, 0.2, 0.4, 0.6, 0.8) lead-free ferroelectric ceramics were prepared via a conventional solid state reaction method. Effects of Co2O3 additive on crystallite structure, microstructure, dielectric and ferroelectric properties of the NBKT–xCo ceramics were studied. X-ray diffraction results showed that the rhombohedral–tetragonal morphotropic phase boundary existed in all the ceramics, with relative amount of tetragonal phase varying with the content of Co2O3. Average grain size, maximum value of dielectric constant, Curie temperature and ferroelectric properties of the ceramics were close related to the content of Co2O3. The dielectric anomaly caused by the phase transition between the ferroelectric phase and the so-called “intermediate phase” was observed in the ceramics with x≤0.2, while it disappeared with further increasing x. All the ceramics showed a diffuse phase transition between the “intermediate phase” and the paraelectric phase. The change in the ferroelectric properties with changing the content of Co2O3 was discussed by considering the competitive effects among grain size, relative amount of the tetragonal phase and oxygen vacancies.