Dielectric-spectroscopic and a.c. conductivity studies on layered Na2-XKXTi3O7 (X=0.2, 0.3, 0.4) ceramics Original Research Article

The dependence of loss tangent (tanδ) and relative permittivity (εr) on temperature and frequency has been reported for Na2-XKXTi3O7 (with X=0.2, 0.3, 0.4) ceramics. The losses are characteristic of dipole mechanism and electrical conduction. The peaks of εr at high temperature indicate a possible ferroelectric phase transition for all three compositions. The results of a.c. conductivity studies on the same samples have also been reported. The corresponding ln(σT) versus 1000/T plots have been divided into five regions namely I, II, III, IV and V. The various conduction mechanisms in the different regions have been stressed. Furthermore, the log(σ) versus frequency plots for all the above samples reveal that the electronic hopping (polaron) conduction, which diminishes with the rise in temperature, is dominant in the lower temperature region. The interlayer ionic conduction seems to play a major role in conduction towards higher temperature.