A re-evaluation of the heat capacity of cerium zirconate (Ce2Zr2O7) Original Research Article

The heat capacity of cerium zirconate pyrochlore, Ce2Zr2O7, was measured from 0.4 to 305 K by hybrid adiabatic relaxation method for various magnetic field strengths. Magnetisation measurements were performed on the sample also. The results revealed a low-temperature anomaly that showed Schottky-type characteristics with increasing magnetic field strength. The estimated entropy due to the magnetic ordering of the two Ce3+ moments is 1.37R, close to the theoretical value for a doublet ground state (1.39R). The enthalpy increments relative to 298.15 K were measured by drop calorimetry from 531 to 1556 K. The obtained results significantly differ from those reported in the literature; the origin of the discrepancy is due to the probable oxidation of the pyrochlore structure into fluorite.