Photoelectrochemical characterization of annealed cadmium selenide photoelectrode using sulphide–polysulphide electrolyte Original Research Article

Cadmium selenide films have been synthesized by dip method. Cadmium selenide acts as photoanode in photoelectrochemical (PEC) cells. The photoanode was annealed upto 473 K. The cell configuration is n-CdSe∣NaOH (1 M) +S (1 M) +Na2S (1 M) ∣C(graphite). Various performance parameters were examined with respect to annealed temperature. It is found that the fill factor and efficiency are maximum for photoelectrode annealed at 473 K. This is due to low resistance, high flat-band potential, maximum open-circuit voltage as well as maximum short-circuit current. The barrier height was examined from the temperature dependence of the reverse saturation current. The lighted ideality factor was found to be minimum for photoelectrode annealed at 473 K. A cell utilizing annealed photoelectrode showed a wider spectral response. The utility of this work is in improving the efficiency of PEC cells.