Fabrication of self-assembled ultrathin photochromic films containing mixed-addenda polyoxometalates H5[PMo10V2O40] and 1,10-decanediamine

A layered phosphovanadomolybdate/1,10-decanediamine (1,10-DAD) self-assembled ultrathin film was fabricated by means of alternating adsorption of mixed-addenda polyoxometalates (POMs) (phosphovanadomolybdate, H5[PMo10V2O40]) and 1,10-DAD, and its photochromic properties were investigated. It is found that the self-assembled multilayer (SAM) film shows high-photochromic response, excellent photochromic stability and reversibility. The photochromic behavior of the SAM is closely related to the reduction potentials of addenda atoms in mixed-addenda POMs. In the case of photo-reduced mixed-addenda POMs, the electron is localized on the more reducible atom, and the addenda atoms with higher reduction potentials show prior photochromism compared with those with lower reduction potentials. The coloration speed is improved after introduction of V into molybdenum POM. The well-ordered lamellar structure of the film was well maintained during the coloration.