Volume conservation during irradiation growth of Zr–2.5Nb

Dimensional changes are reported in three dimensions for cold-worked Zr–2.5 Nb pressure tube material irradiated to a fast fluence of 174 × 1024 nm−2, E > 1 MeV at a nominal temperature of 250 °C. The observed dimensional changes in the longitudinal and transverse directions (up to ∼1.2% and ∼−0.5%, respectively) are consistent with earlier data at 280 °C and 310 °C, and the previously reported negative temperature dependence. The observed growth in the radial direction is negative (up to ∼0.7%). Initially, there is a small volume increase (0.05–0.1%) but this gradually decays to < 0.05% and the long term rate of volume change is negligible, within the accuracy of the measurement, demonstrating that the phenomenon observed is, indeed, irradiation growth.