Radiation-induced stress relaxation in high temperature water of type 316L stainless steel evaluated by neutron diffraction

Weld beads on plate specimens made of type 316L stainless steel were neutron-irradiated up to about 2.5 × 1025 n/m2 (E > 1 MeV) at 561 K in the Japan Material Testing Reactor (JMTR). Residual stresses of the specimens were measured by the neutron diffraction method, and the radiation-induced stress relaxation was evaluated. The values of σx residual stress (transverse to the weld bead) and σy residual stress (longitudinal to the weld bead) decreased with increasing neutron dose. The tendency of the stress relaxation was almost the same as previously published data, which were obtained for type 304 stainless steel. From this result, it was considered that there was no steel type dependence on radiation-induced stress relaxation. The neutron irradiation dose dependence of the stress relaxation was examined using an equation derived from the irradiation creep equation. The coefficient of the stress relaxation equation was obtained, and the value was 1.4 (×10−6/MPa/dpa). This value was smaller than that of nickel alloy.